Sika MonoTop®-4012 BE

• VOC emission classification GEV EMICODE EC1^plus

• Eurofins VOC Emission Indoor Air Comfort Gold Sika MonoTop®-4012 BE

• Specific electrical resistivity according to CROW-CUR-Recommendation 130:2024 , Sika MonoTop®-4012 BE 

• Contributes towards satisfying Materials and Resources (MR) Credit: Building product disclosure and optimization — Environmental Product Declarations under LEED® v4 — 1 point

• Contributes towards satisfying Materials and Resources (MR) Credit: Building Product Disclosure and Optimization — Sourcing of Raw Materials under LEED® v4 — 1 point

• Contributes towards satisfying Materials and Resources (MR) Credit: Building Product Disclosure and Optimization — Material Ingredients under LEED® v4 — 1 point

• Environmental Product Declaration (EPD) in accordance with EN 15804. EPD independently verified by Institut für Bauen und Umwelt e.V. (IBU)

   

• CE marking and declaration of performance based on EN 1504-3:2005 Products and systems for the protection and repair of concrete structures — Structural and non-structural repair

Sulphate resistant and replacement cement, selected aggregates and additives 

12 months from date of production

The product must be stored in original, unopened and undamaged packaging in dry conditions at temperatures between +5 °C and +30 °C. Always refer to packaging.

D_max: 2 mm

Class R4

3,50 to 3,75 L of water for 25 kg bag

+5 °C minimum / +30 °C maximum 

+5 °C minimum / +30 °C maximum

~ 60 minutes (+20 °C)

~2,2 kg/l

~ 1,90 kg/m²/mm

Consumption depends on the roughness and absorbency of the substrate. This figure is theoretical and does not allow for any additional material due to surface porosity, surface profile, variations in level or wastage etc.

25 kg of powder yields ~13,2 L of mortar

Select the most appropriate equipment required for the project:

Substrate preparation

• Mechanical hand held tools
• High / ultra-high pressure water blasting equipment

Steel reinforcement

• Abrasive blast cleaning equipment
• High pressure water blasting equipment

Mixing

• Small quantities - low speed electric single or double paddle mixer (<500 rpm). Mixing Container.
• Large quantities or machine application - suitable forced action mixer

Application

• Hand applied – Plasterers hawk, trowel
• Wet Spray - All in one mixing and spraying machine or separate spraying machine and all associated ancillary equipment to suit application volumes

Finishing

• Trowel ( PVC or wooden),sponge

Also refer to Site Handbook ‘Repair of Concrete Structures – Patch Repair and Spray Applications’ 

Hand applied and wet spray application

Pour the minimum recommended clean water quantity into a suitable mixing container / equipment. While stirring slowly, add the powder to the water and mix thoroughly for at least for 3 minutes adding additional water if necessary to the maximum specified amount and adjust to the required consistency to achieve a smooth consistent mix. The consistency must be checked after every mix.

Strictly follow installation procedures as defined in method statements, application manuals and working instructions which must always be adjusted to the actual site conditions.

Reinforcement corrosion protection coating

Where a reinforcement coating is required, apply to the whole exposed circumference Sika MonoTop®- 1010 or SikaTop® Armatec® 110 EpoCem® (Refer to Product Data Sheet(s)).

Bonding primer

On a well prepared and roughened substrate or for a sprayed application, a bonding primer is generally not required. When a bonding primer is required to achieve the required adhesion values, use Sika MonoTop®-1010 or SikaTop® Armatec® 110 EpoCem® (Refer to respective Product Data Sheets). Apply repair mortar onto bonding primer “wet on wet”.

Repair Mortar

Hand application

Thoroughly pre-wet the prepared substrate (2 hours recommended) before application. Keep the surface wet and do not allow to dry. Before application remove excess water, e.g. with a clean sponge. The surface must appear a dark matt appearance without shining and surface pores and cavities must not contain water.

When manually applying by hand, first make a scratch coat by firmly scraping the repair mortar over the substrate surface to form a thin layer and fill any pores or cavities in the surface. Ensure the whole surface to be repaired is covered by the scratch coat. The repair mortar must be applied onto the wet scratch coat between the minimum and maximum layer thicknesses without the formation of voids. Where layers are to be built up, to prevent sagging or slumping, each layer should be allowed to harden before applying subsequent layers “wet on wet”.

Sprayed application - Wet Spray

The wet mixed Sika MonoTop®-4012 BE must be placed into the spraying equipment and applied onto the pre-wetted substrate (pre-wet procedure as hand application) between the minimum and maximum layer thicknesses without the formation of voids. Where layers are to be built up, to prevent sagging or slumping, each layer must be allowed to harden before applying subsequent layers “wet on wet”.

Surface finishing

Finishing for all types of application must be carried out to the required surface texture using suitable finishing tools as soon as the mortar has started to harden.

Cold weather working

Consider storing bags in a warm environment and using warm water to assist with achieving strength gain and maintaining physical properties.

Hot weather working

Consider storing bags in a cool environment and using cold water to assist with controlling the exothermic reaction to reduce cracking and maintaining physical properties. 

Protect fresh mortar immediately from premature drying using an appropriate curing method, e.g. curing compound, moist geotextile membrane, polythene sheet, etc.

Curing compounds must not be used when they could adversely affect subsequently applied products and systems

Clean all tools and application equipment with water immediately after use. Hardened material can only be mechanically removed.