Product Data Sheet Show all documents
Sika® Igolflex®-201

Sika® Igolflex®-201

2-part polymer modified bituminous thick coating

Sika® Igolflex®-201 is a 2 component polymer modified bituminous flexible thick coating extended with fibre for waterproofing against dampness and moisture ingress.

  • Non-flammable
  • Flexible with crack-bridging capabilities
  • Fast curing time
  • Used as adhesive for thermal insulation boards
  • Can be applied on dry and slightly damp surfaces
  • Easy to apply by notched trowel
  • Non-sag on vertical surfaces
Send us an enquiry
Product Data Sheet Show all documents

Usage

  • Waterproofing and damp proofing of below ground concrete structures to protect against percolating water, dampness and moisture ingress
  • Waterproofing beneath cementitious floor screeds
  • Adhesive to bond lightweight thermal insulation boards
 

Advantages

  • Non-flammable
  • Flexible with crack-bridging capabilities
  • Fast curing time
  • Used as adhesive for thermal insulation boards
  • Can be applied on dry and slightly damp surfaces
  • Easy to apply by notched trowel
  • Non-sag on vertical surfaces

Packaging

32 kg combi-unit:

Part A - Liquid

24 kg

Part B - Powder

8 kg

Refer to current price list for packaging variations.

Colour

Part A

Black

Part B

Grey

Product Details

Sustainability / Certifications / Approvals

APPROVALS / STANDARDS

  • CE Marking and Declaration of Performance to EN 15814 - Polymer modified bituminous thick coatings for waterproofing in below ground structures
Product Information

Chemical Base

Polymer modified and fibre reinforced bitumen emulsion and a reactive hydraulic binder.

Shelf Life

12 months from date of production

Storage Conditions

The product must be stored in original, unopened and undamaged sealed packaging in dry conditions at temperatures between +5 °C and +30 °C. Always refer to packaging.

Density

Part A

~1,03 kg/l

Part B

~1,30 kg/l

Mixed A + B

~1,17 kg/l

 
Technical Information

Crack Bridging Ability

Class CB 2

No damage

(for crack width ≥ 2 mm and dry layer thickness ≥ 3 mm)

Chemical Resistance

Resistant to aggressive substances in natural ground water and soil. Contact Sika Technical Services for additional information.

Permeability to Water Vapour

µ ≥ 38 000

(DIN EN 12086)

Sd ≥ 117 m

(DIN EN 1931)

Water Tightness

Class W2A

Pass

(≥ 72 h at 0,075 N/mm2 for dry layer thickness with inlay ≥ 4 mm)

Reaction to Fire

Class E

(EN 13501-1)

Application

Application Information

Mixing Ratio

Part A : Part B = 3 : 1 (by weight) 

Layer Thickness

Refer to national and local standard.

Minimum recommendations:

Damp proofing

3 mm dry film (one layer)

Waterproofing

4 mm dry film in two layers with an inlay of Sika® Igolflex® F-01

Ambient Air Temperature

+5 °C min. / +35 °C max.

Substrate Temperature

+5 °C min. / +35 °C max.

Substrate Moisture Content

 Dry or slightly damp

Pot Life

~1,5 hours (at +20 °C), depends on ambient conditions.

Curing Time

Fully cured: ~2 to 3 days.

Times are approximate and will be affected by substrate, film thickness and changing ambient conditions particularly temperature and relative humidity.

Waiting Time / Overcoating

Sika® Igolflex®-201 on Sika® Igolflex®-201: Within 2 to 4 hours.

Times are approximate and will be affected by substrate, film thickness and changing ambient conditions particularly temperature and relative humidity.
Consumption

Consumption

Consumption depends on the roughness and absorbency of the substrate.
 

Damp proofing

~4,5 to 5,0 kg/m2

(~4,5 to 5,0 mm wft)

(3,1 to 3,4 mm dft)

Waterproofing

~6,0 to 6,5 kg/m2

(~6,0 to 6,5 mm wft)

(4,4 to 4,7 mm dft)

Adhesive for boards

~2,0 kg/m2

These figures are theoretical and do not allow for any additional material due to surface porosity, surface profile, variations in level or wastage etc.
Application steps

SUBSTRATE QUALITY

Substrate must be uniform, dry or slightly damp, free from dust, loose material, surface contamination, existing coatings, oil, grease and other materials which could reduce adhesion of the coating. Surface defects (>5 mm) such as blowholes, voids, honeycombing, etc. must be filled / repaired with suitable Sika® repair mortars.

SUBSTRATE PREPARATION

Surfaces must be cleaned and prepared using suitable preparation techniques to provide a clean slightly textured surface. Defects should be repaired with an appropriate Sika® repair mortar. Porous substrates must be primed using Sika® Igolflex ® P-01 or use diluted Sika® Igolflex®-101. Sika® Igolflex®-101 : Water (1:2 by weight).

MIXING

Prior to mixing all parts, mix part A (resin) using an electric single paddle mixer (300–400 rpm) or other similar equipment. Mix liquid and all the coloured pigment until a uniform colour / mix has been achieved. Add part B (hardener) to part A and mix part A + B continuously for at least 3 minutes until a uniformly coloured mix has been achieved. Excessive mixing must be avoided to minimise air entrainment. During the final mixing stage, scrape down the sides and bottom of the mixing container with a straight edge trowel or spatula at least once to ensure complete mixing. Mix full units only. Mixing time for A+B = ~3 minutes.

CLEANING OF TOOLS

Clean all tools and application equipment with water immediately after use. Hardened Sika® Igolflex®-201 can be removed with Sika® Thinner C.

 