SikaSeal®-175

• VOC emission classification GEV Emicode EC1^plus

• CE marking and declaration of performance based on EN 15651-3:2012 Sealants for non-structural use in joints in buildings and pedestrian walkways — Part 3: Sealants for sanitary joints

Alkoxy silicone

18 months from date of production

The Product must be stored in original, unopened and undamaged sealed packaging in dry conditions at temperatures between +5 °C and +25 °C. Always refer to packaging.

Refer to the current Safety Data Sheet for information on safe handling and storage.

The joint dimensions must be designed to suit the movement capability of the sealant. For joint widths more than 10 mm and less than 20 mm, the minimum joint depth is 10 mm.

For larger joints, contact Sika Technical Services for additional information.

Beware of condensation. Substrate temperature during application must be at least +3 °C above dew point.

Use closed cell, polyethylene foam backing rod or backing tape.

The Product must not be used on the following substrates:

• Pre-stressed polyacrylate or polycarbonate

• Bitumen, natural rubber or EPDM

On the following substrates, the Product may exhibit poor adhesion:

• Polyethylene (PE)

• Polypropylene (PP)

• PTFE (Teflon®)

Perform a preliminary adhesion test on the above substrates before full application.

Contact Sika Technical Services for additional information.

Inadequate surface preparation

Note: Primers are adhesion promoters and not an alternative to improve poor preparation or cleaning of the joint surface. Primers also improve the long term adhesion performance of the sealed joint.

Substrate testing

Note: Adhesion tests on project specific substrates must be performed and procedures agreed with all parties before full project application. For more detailed advice and instructions contact Sika Technical Services.

The substrate must be sound, clean, dry and free of contaminants such as dirt, oil, grease, cement laitance, sealant residues and poorly bonded coatings which could affect adhesion of the primer and sealant.

The substrate must be of sufficient strength to cope with the stresses induced by the sealant during movement.

1. Use techniques such as wire brushing, grinding, grit blasting or other suitable mechanical tools to remove all weak substrate material.
2. Repair all damaged joint edges with suitable Sika repair products.
3. Remove all dust, loose and friable material from all surfaces before application of the sealant.

If tested or supported by experience, the Product can be used without primers or activators on many substrates.

NON-POROUS SUBSTRATES

Aluminium, anodised aluminium, stainless steel, galvanised steel, powder coated metals, glazed tiles, or other metals, such as copper, brass and titanium-zinc.

1. Lightly roughen the surface with a fine abrasive pad.
2. Clean and pre-treat using Sika® Aktivator-205 with a clean cloth. Wait until the flash off time has been achieved.
3. Apply Sika® Primer-3 N by brush.

PVC substrates.

1. Lightly roughen the surface with a fine abrasive pad.
2. Clean and pre-treat using Sika® Aktivator-205 with a clean cloth. Wait until the flash off time has been achieved.
3. Clean and pre-treat using Sika® Primer-215 applied with a brush.

Glass substrates

1. Clean and pre-treat using Sika® Cleaner P applied with a clean cloth and wait until the flash off time has been achieved.

POROUS SUBSTRATES

Concrete, aerated concrete and cement based renders, mortars and bricks.

1. Prime surface using Sika® Primer-3 N applied by brush.

For more details of the primer or pre-treatment products refer to the individual Product Data Sheet. Contact Sika Technical Services for additional information.

IMPORTANT

Strictly follow installation procedures

Strictly follow installation procedures as defined in Method Statements, application manuals and working instructions which must always be adjusted to the actual site conditions.

IMPORTANT

Absorbency of natural stone substrates

Staining from plasticiser migration may occur when used on natural stone such as granite, marble or limestone substrates.

1. Carry out preliminary trials before full project application.
2. Contact Sika Technical Services for further advice.

IMPORTANT

Application in confined spaces

Atmospheric moisture is required for the Product to cure.

1. Do not use in a totally confined space.

Preconditions

The flash-off time of the primer has been achieved.

1. Apply masking tape where neat or exact joint lines are required.
2. After the required substrate preparation, insert a backing rod to the required depth.

3. Prime the joint surfaces as recommended in substrate preparation.

   Note: Avoid excessive application of primer to avoid causing puddles at the base of the joint.
4. Open the seal on the top of the cartridge, or open the end of the foil pack. Fit the nozzle and cut it to the desired size. Insert the product into the caulking gun.
5. Apply the Product into the joint ensuring that it comes into full contact with the sides of the joint and avoiding any air entrapment.
6. IMPORTANT Do not use tooling products containing solvents. As soon as possible after application, tool the sealant firmly against the joint sides to ensure adequate adhesion and a smooth finish. Use a compatible tooling agent such as Sika® Tooling Agent N to smooth the joint surface.
7. Remove the tape within the skinning time of the Product after finishing.

Colour variation

Note: Colour variations may occur due to the exposure in service to chemicals, high temperatures or UV-radiation, especially with white colour shade. This effect is aesthetic and does not adversely influence the technical performance or durability of the product.

Clean all tools and application equipment immediately after use with Sika® Remover-208. Once cured, hardened material can only be removed mechanically. For cleaning skin use Sika® Cleaning Wipes-100.