Sikaplan® SGK-18
Sikaplan® SGK-18 is a multi-layer, synthetic roof waterproofing sheet based on premium-quality polyvinyl chloride (PVC) with inlay of glass non-woven and polyester fleece backing according to EN 13956.
- Resistant to permanent UV irradiation
- High dimensional stability due to glass fleece inlay
- Resistant against impact load and hail
- High water vapour permeability
- Resistant to all common environmental influences
- Compatible to old bitumen due to felt backing
- Hot air welding without use of open flames
- Recyclable
Usage
Roof waterproofing membrane for exposed flat roofs, adhered by using Sika-Trocal® C-300 adhesive. Approved Substrates:- Slated/mineralized bitumen sheets; new and aged
- EPS: compressive strength ≥ 100 kPa (10 %), Density >20 kg/m3
- OSB, plywood, fibre cement boards
- Mineral fibre boards (e.g. Bondrock MV)
- PUR/PIR insulation boards, (e.g. Sarnatherm PIR GT, Kingspan TR 27)
- Concrete, lightweight concrete
- Metal
Advantages
- Resistant to permanent UV irradiation
- High dimensional stability due to glass fleece inlay
- Resistant against impact load and hail
- High water vapour permeability
- Resistant to all common environmental influences
- Compatible to old bitumen due to felt backing
- Hot air welding without use of open flames
- Recyclable
Packaging
Packing unit: | see price list |
Roll length: | 12.50 m |
Roll width: | 2.00 m |
Roll weight: | 62.50 kg |
Colour
Surface: | slightly structured |
Colours: | |
Top surface: | light grey (nearest RAL 7047) |
Bottom surface: | lead grey (nearest RAL 7012) |
Product Details
APPROVALS / STANDARDS
- Polymeric sheets for roof waterproofing according to EN 13956, certified by notified body 1213-CPD-4125 and provided with the CE marking.
- Reaction to fire according to EN 13501-1.
- External fire performance tested according to ENV 1187 and classified according to EN 13501-5: BROOF(t1) and BROOF(t3).
- Official Quality Approvals and Agrement Certificates and approvals.
- Monitoring and assessment by approved laboratories.
- Quality Management system in accordance with EN ISO 9001/14001.
- Production according to Responsible Care policy of Chemical Industry.
Product Declaration
EN 13956
Shelf Life
5 years from date of production in unopened, undamaged and original packaging.Product does not expire during correct storage.
Storage Conditions
Rolls must be stored between +5 °C and +30 °C in a horizontal position on pallet, protected from direct sunlight, rain and snow. Do not stack pallets of rolls or any other material during transport or storage.
Visible Defects
Pass | (EN 1850-2) |
Length
12.50 m (-0 % / +5 %) | (EN 1848-2) |
Width
2.00 m (-0.5 % / +1 %) | (EN 1848-2) |
Effective Thickness
1.8 mm (-5 % / +10 %) | (EN 1849-2) |
Straightness
≤ 30 mm | (EN 1848-2) |
Flatness
≤ 10 mm | (EN 1848-2) |
Mass per unit area
2.5 kg/m2 (-5 % / +10 %) | (EN 1849-2) |
System Structure
The following accessories shall be used:
- Sikaplan® D-18 or Sikaplan® S-15 unreinforced sheet for detailing.
- Sikaplan® G-15 or Sikaplan® SG-15 roofing sheet for stripes.
- Moulded corner pieces, prefabricated corners and pipe flashings
- Sika-Trocal® Metal Sheet Type S
- Sarnabar for peel stop
- Sika-Trocal® Cleaner-2000
- Sika-Trocal® Cleaner L-100
- Sika-Trocal® Welding Agent
- Sika-Trocal® Seam Sealant
- Sika-Trocal® C-300 (One-component PU adhesive for surface bonding)
- Sika-Trocal® C-733 (Contact adhesive)
Compatibility
The PVC compound is not compatible with direct contact to other plastics, e.g. EPS, XPS, PUR, PIR or PF.
The PVC compound is not resistant to tar, bitumen, oil and solvent containing materials.
Compatibility to bitumen or plastic surfaces below the membrane is achieved by incorporated Polyester fleece backing.
Resistance to Impact
hard substrate | ≥ 800 mm |
soft substrate | ≥ 1500 mm |
Hail Resistance
rigid substrate | ≥ 25 m/s |
flexible substrate | ≥ 32 m/s |
Tensile Strength
longitudinal (md)1) | ≥ 600 N/50 mm |
transversal (cmd)2) | ≥ 600 N/50 mm |
1) md - machine direction
2) cmd - cross machine direction
Elongation
longitudinal (md)1) | ≥ 50 % |
transversal (cmd)2) | ≥ 50 % |
1) md - machine direction
2) cmd - cross machine direction
Tear Strength
longitudinal (md)1) | ≥ 150 N |
transversal (cmd)2) | ≥ 150 N |
1) md - machine direction
2) cmd - cross machine direction
Joint Peel Resistance
≥ 300 N/50 mm | (EN 12316-2) |
Joint Shear Resistance
≥ 500 N/50 mm | (EN 12317-2) |
Dimensional Stability
longitudinal (md)1) | ≤ |0.3| % |
transversal (cmd)2) | ≤ |0.3| % |
1) md - machine direction
2) cmd - cross machine direction
Foldability at Low Temperature
≤ -25°C | (EN 495-5) |
Water Tightness
Pass | (EN 1928) |
Effect of Liquid Chemicals, Including Water
On request | (EN 1847) |
UV Exposure
Pass (> 5 000 h / grade 0) | (EN 1297) |
External Fire Performance
BROOF(t1)<20°, < 20°, BROOF(t3) <10° / <70° | (EN 13501-5) |
Reaction to Fire
Class E | (EN ISO 11925-2, classification to EN 13501-1) |
Application
Ambient Air Temperature
-15 °C min. / +60 °C max. for hot air welding
+5 °C min. / +60 °C max. for cold welding
Substrate Temperature
-25 °C min. / +60 °C max. for hot air welding
+5 °C min. / +60 °C max. for cold welding
SUBSTRATE QUALITY
The substrate surface must be uniform, smooth and free of any sharp protrusions or burrs, etc.
In case of adhesion by Sika-Trocal® C-300, all layers of the built-up and substrate must be secured against wind uplift.
The Polyester fleece laminated to Sikaplan® SGK-18 underside separates sufficiently from any incompatible substrate. It prevents from direct contact to bitumen or plastic material, e.g. expanded polystyrene (EPS), extruded polystyrene (XPS), polyurethane (PUR), polyisocyanurate (PIR) or phenolic foam (PF) for compatibility in the built-up.
APPLICATION
Installation works must be carried out only by Sika instructed contractors for roofing.
Installation of some ancillary products, e.g. contact adhesives/thinners is limited to temperatures above +5 °C. Please refer to the respective Product Data Sheets.
Special measures may be compulsory for installation below +5 °C ambient temperature due to safety requirements in accordance with national regulations.