Product Data Sheet
Show all documents

Sikadur®-330

2-component epoxy impregnation resin

Sikadur®-330 is a 2-component, thixotropic epoxy based impregnating resin and adhesive.

  • Easy mix and application by trowel and impregnation roller
  • Manufactured for manual saturation methods
  • Excellent application behaviour to vertical and overhead surfaces
  • Good adhesion to many substrates
  • High mechanical properties
  • No separate primer required
 
Find a Technical Advisor
Product Data Sheet
Show all documents

Usage

Sikadur®-330 is used as:
  • Impregnation resin for SikaWrap® fabric reinforcement for the dry application method
  • Primer resin for the wet application system
  • Structural adhesive for bonding Sika® CarboDur® plates into slits

Advantages

  • Easy mix and application by trowel and impregnation roller
  • Manufactured for manual saturation methods
  • Excellent application behaviour to vertical and overhead surfaces
  • Good adhesion to many substrates
  • High mechanical properties
  • No separate primer required
 

Packaging

5 kg (A+B)Pre-batched unit

Not pre-dosed industrial packaging:

Component A

24 kg pails

Component B

6 kg pails

Colour

Component A: white paste
Component B: grey paste
Components A + B mixed: light grey paste

Product Details

Sustainability / Certifications / Approvals

ENVIRONMENTAL INFORMATION

  • Conformity with LEED v4 MRc 4 (Option 2): Building Product Disclosure and Optimization - Material Ingredients
  • Conformity with LEED v2009 IEQc 4.1: Low-Emitting Materials - Adhesives and Sealants

APPROVALS / STANDARDS

  • Avis Technique N° 3/16-875 (annule et remplace N° 3/10-669) Sika® CarboDur®, SikaWrap®

  • CIT n°290 18/07/2017 (certificato di idoneità tecnica all'impiego) ; Sika ® CarboDur®, SikaWrap®, Sikadur®

  • Road and Bridges Research Institute (Poland): IBDiM No AT/2008-03-336/1
  • Adhesive for structural bonding tested according to EN 1504-4, provided with the CE-mark
Product Information

Chemical Base

Epoxy resin

Shelf Life

24 months from date of production

Storage Conditions

Store in original, unopened, sealed and undamaged packaging in dry conditions at temperatures between +5 °C and +30 °C. Protect from direct sunlight.

Density

1.30 ± 0.1 kg/l (component A+B mixed) (at +23 °C)

Viscosity

Shear rate: 50 /s

Temperature

Viscosity

+10 °C

~10 000 mPas

+23 °C

~6 000 mPas

+35 °C~5 000 mPas
System information

System Structure

Substrate primer - Sikadur®-330.
Impregnating / laminating resin - Sikadur®-330.
Structural strengthening fabric - SikaWrap® type to suit requirements.
Technical Information

Flexural E-Modulus

~ 3 800 N/mm2 (7 days at +23 °C)(DIN EN 1465)

Tensile Strength

 ~ 30 N/mm2 (7 days at +23°C)(ISO 527)

Tensile Adhesion Strength

Concrete fracture (> 4 N/mm2) on sandblasted substrate

(EN ISO 4624)

Coefficient of Thermal Expansion

4.5 × 10−5 1/K (Temperature range −10 °C − +40 °C)

(EN 1770)

Glass Transition Temperature

Curing time

Curing temperature

TG

30 days

+30 °C

+58 °C

Heat Deflection Temperature

Curing time

Curing temperature

HDT

7 days+10 °C+36 °C
7 days+23 °C+47 °C
7 days+35 °C+53 °C

 Resistant to continuous exposure up to +45 °C.

Service Temperature

–40 °C to +45 °C

Application

Application Information

Mixing Ratio

Component A : component B = 4 : 1 by weight
When using bulk material the exact mixing ratio must be safeguarded by accurately weighing and dosing each component.

Ambient Air Temperature

+10 °C min. / +35 °C max.

Dew Point

Beware of condensation.
Substrate temperature during application must be at least 3 °C above dew point.

Substrate Temperature

+10 °C min. / +35 °C max.

Substrate Moisture Content

< 4 % pbw

Pot Life

Temperature

Pot life

Open time

+10 °C

~90 minutes (5 kg)

~90 minutes
+23 °C~60 minutes (5 kg)~60 minutes

+35 °C

~30 minutes (5 kg)

~30 minutes

The pot life begins when the resin and hardener are mixed. It is shorter at high temperatures and longer at low temperatures. The greater the quantity mixed, the shorter the pot life. To obtain longer workability at high temperatures, the mixed adhesive may be divided into portions. Another method is to chill components A+B before mixing them (not below +5 °C).
Consumption

Consumption

See the "Method Statement for SikaWrap® manual dry application" Ref 850 41 02.
Guide: 0.7 - 1.5 kg/m2
Application steps

SUBSTRATE QUALITY

Substrate must be sound and of sufficient tensile strength to provide a minimum pull off strength of 1.0 N/mm2 or as per the requirements of the design specification.
See also the "Method Statement for SikaWrap® manual dry application" Ref 850 41 02.

SUBSTRATE PREPARATION

See the "Method Statement for SikaWrap® manual dry application" Ref 850 41 02.

MIXING

Pre-batched units:
Mix components A+B together for at least 3 minutes with a mixing spindle attached to a slow speed electric drill (max. 300 rpm) until the material becomes smooth in consistency and a uniform grey colour. Avoid aeration while mixing. Then, pour the whole mix into a clean container and stir again for approx. 1 more minute at low speed to keep air entrapment at a minimum. Mix only that quantity which can be used within its pot life.

 
Bulk packing, not pre-batched:
First, stir each component thoroughly. Add the components in the correct proportions into a suitable mixing pail and stir correctly using an electric low speed mixer as above for
pre-batched units.

CLEANING OF TOOLS

Clean all equipment immediately with Sika® Colma Cleaner. Cured material can only be removed mechanically.

 