Sikafloor® Pronto RS-34
Sikafloor® Pronto RS-34 is a decorative, fast curing, acrylic resin flooring system. The fast curing allows full use of the floor within hours of application.
- Seamless
- Very fast curing at low temperatures
- High mechanical resistance
- Low maintenance
- Colour options
- Decorative design
- Chemical resistant top coat
- Easy application
- Lightly textured semi-gloss finish
- Thickness: ~2,0–4,0 mm
System Structure
1
Primer
2
Wearing coat & broadcasting with flakes
Usage
- Manufacturing facilities where minimum downtime of the production process is required.
- Facilities in the food and beverage industry with a demand for fast curing and chemically resistant floors
- For interior use
Advantages
- Seamless
- Very fast curing at low temperatures
- High mechanical resistance
- Low maintenance
- Colour options
- Decorative design
- Chemical resistant top coat
- Easy application
- Lightly textured semi-gloss finish
- Thickness: ~2,0–4,0 mm
Packaging
Refer to the individual product data sheets
Colour
Standard colour: ~RAL 7032. Other colours on request.
Appearance
Lightly textured semi-gloss finish
System Details
System Structure
Sikafloor® Pronto RS-34 system (~2–4 mm)
Layer | TProduct |
1. Primer | Sikafloor®-10/-11/-13 Pronto |
2. Wearing layer + Coloured flake broadcast | Sikafloor®-14 Pronto (filled 1:2 with Sikafloor® Pronto Filler) + coloured flakes |
3. Seal / Top coat | Sikafloor®-16 Pronto |
Composition
Reactive acrylic resins
Nominal Thickness
~2–4 mm
Shelf Life
Refer to the individual product data sheets
Storage Conditions
Refer to the individual product data sheets
Chemical Resistance
Sikafloor®-16 Pronto provides the chemical resistance. Refer to Product Data Sheet.
Application
Ambient Air Temperature
0 °C min. / +30 °C max.
Relative Air Humidity
80 % max.
Dew Point
Beware of condensation.
The substrate and uncured applied floor material must be at least +3 °C above dew point to reduce the risk of condensation or blooming on the surface of the applied product.
Substrate Temperature
0 °C min. / +30 °C max.
Substrate Moisture Content
≤4 % parts by weight
The following test methods can be used: Sika®-Tramex meter, CM - measurement or Oven-dry-method. No rising moisture according to ASTM (Polyethylene-sheet).
Waiting Time / Overcoating
Before applying Sikafloor®-14 Pronto on Sikafloor®-11/-13 Pronto allow:
Substrate temperature | Minimum |
0 °C | 50 min |
+10 °C | 45 min |
+20 °C | 40 min |
+30 °C | 35 min |
Before applying Sikafloor®-14 Pronto on Sikafloor®-10 Pronto allow:
Substrate temperature | Minimum |
0 °C | 70 min |
+10 °C | 50 min |
+20 °C | 50 min |
+30 °C | 35 min |
Before applying Sikafloor®-16 Pronto on Sikafloor®-14 Pronto allow:
Substrate temperature | Minimum |
-5 °C | 120 min |
0 °C | 80 min |
+10 °C | 60 min |
+20 °C | 45 min |
+30 °C | 30 min |
Times are approximate and will be affected by changing ambient conditions particularly temperature and relative humidity.
Applied Product Ready for Use
Temperature | Foot traffic | Full traffic |
- 5 °C | ~70 min | ~2 h |
0 °C | ~50 min | ~2 h |
+10 °C | ~50 min | ~1 h |
+20 °C | ~40 min | ~1 h |
+20 °C | ~30 min | ~1 h |
Times are approximate and will be affected by changing ambient conditions particularly temperature and relative humidity.
Consumption
Sikafloor® Pronto RS-34 system (~2–4 mm)
Layer | Product | Consumption |
1. Primer | 1–2 × Sikafloor®-10/-11/-13 Pronto | 1–2 × ~0,4–0,5 kg/m² |
Optional* -Levelling Mortar (surface roughness up to 3 mm) | Sikafloor®-11 Pronto filled 1:1,5–2,0 with Sikafloor® Pronto Filler by weight | 1,6 kg/m²/mm |
2. Wearing layer + | Sikafloor®-14 Pronto filled 1:2 with Sikafloor® Pronto Filler by weight | ~3,6 kg/m² |
Coloured flake broadcast | Coloured flakes | ~0,5-1,0 kg/m² |
3. Seal / Top coat | Sikafloor®-16 Pronto | 1–2 × ~0,6–0,8 kg/m² |
*Not included in the system structure diagram.
These figures are theoretical and do not allow for any additional material due to surface porosity, surface profile, variations in level or wastage etc.
CLEANING
Refer to Sika Method Statement: Sikafloor®-Cleaning Regime