Sikafloor® MultiFlex PS-27 ESD
The Sikafloor® MultiFlex PS-27 ESD system is a seamless, smooth, low voc, polyurethane, coloured, matt ESD floor covering. It consist out of the two part, self-smoothing, polyurethane coating Sikafloor®-327 and the two part, water dispersed, coloured ESD polyurethane roller coating Sikafloor®-305 W ESD.
- Very low VOC emissions
- Water based
- Easy to apply
- Easy to refurbish, can be overcoated directly with itself
- Low odour
- Good UV resistance, non-yellowing
- Easy to clean
- Conforms to the requirements of ANSI/ESD S20.20 and IEC 61340-5-1
- Matt surface
- Suitable as floor covering acc. DIN VDE 0100-410 / T610 as top coat of non-conductive Sikafloor® products
System Structure
1
Base coat
2
Final conductive coating
Usage
It is used as:- Dissipative coloured indoor system for electrostatic protected areas (EPA).
- Particularly suitable for areas with requirements for the lowest electrostatic charge (low BVG (Body Voltage Generation)) and dissipative surface
- Typical applications include clean rooms in the electronics industry, microbiology/microchemistry sectors, production plants in the automobile industry etc.
Advantages
- Very low VOC emissions
- Water based
- Easy to apply
- Easy to refurbish, can be overcoated directly with itself
- Low odour
- Good UV resistance, non-yellowing
- Easy to clean
- Conforms to the requirements of ANSI/ESD S20.20 and IEC 61340-5-1
- Matt surface
- Suitable as floor covering acc. DIN VDE 0100-410 / T610 as top coat of non-conductive Sikafloor® products
Packaging
Please refer to individual Product Data Sheet.
Colour
Available in a limited number of colour shades such as RAL 1000, 1001, 1002, 1011, 3012, 5024, 6021, 6024, 7032, 7035, 7038, 7040, 7042, 7044, 7047, 9018.
Be aware that the colour of the layer below has to be approx. adjusted to the colour of the Sikafloor®-305 W ESD.
Appearance
Matt
System Details
APPROVALS / STANDARDS
- Synthetic resin screed material according to EN 13813:2002, Declaration of Performance and provided with the CE mark
- Coating for surface protection of concrete according to EN 1504-2:2004, Declaration of Performance and provided with the CE mark
- Test of floors regarding ESD-protective properties, SP-Technical Research Institute of Sweden, Report No. 5F005664:A and No. 5F005664:B
- Approval for ESD products according to IEC 61340, SP-Technical Research Institute of Sweden, No. 230-15-0020, rev 1
- Varnishability test acc. to VW-standard PV 3.10.7, Report No. 14-04-14201871-19
- Slip resistance test acc. DIN 51130, Report No. 020143-15-10, Test Institute Roxeler
- Fire classification acc. to DIN EN 13501-1, Test reports KB-Hoch-150461-2, Test Institute Hoch, DE-Fladungen
- Fire classification acc. to DIN EN ISO 9239-1, Test reports KB-Hoch-150460-2, Test Institute Hoch, DE-Fladungen
- Fire classification acc. to DIN EN 11925-2, Test reports KB-Hoch-150459-2, Test Institute Hoch DE-Fladungen
- Test of the Insulation Resistance acc. DIN VDE 0100-410/T610. Test Report P 9915-E, Kiwa-Polymer Institut
- Outgassing emission certificate Sikafloor-305 W ESD: CSM Statement of Qualification - ISO 14644-8, class -9.6 - Report No. SI 1506-767, Frauenhofer IPA
- Biological Resistance in accordance with ISO 846, CSM Report No. SI 1506-767, Frauenhofer IPA
System Structure
Sikafloor® MultiFlex PS-27 ESD:
1. Primer | Sikafloor®-156/-160/-161 |
2- Base coat + Earthing connection | Sikafloor®-327 + Sika® Earthing Kit |
3. Final conductive coating | Sikafloor®-305 W ESD |
The system configuration as described must be fully complied with and may not be changed.
Composition
PUR
Nominal Thickness
~ 1.5 - 2.0 mm
Volatile organic compound (VOC) content
Very low content of volatile organic compounds. Sikafloor®-305 W ESD, the finishing layer of the Sikafloor® MultiFlex PS-27 ESD System, has been awarded the Frauenhofer IPA CSM Certicate of Qualification with the report number SI 1506-767. The Outgassin test was performed in accordance with CSM procedures. TVOC: ISO-AMC Class -9.6 (see ISO 14644-8).
Shelf Life
Please refer to individual Product Data Sheet.
Storage Conditions
Please refer to individual Product Data Sheet.
Tensile Adhesion Strength
> 1.5 N/mm² | (ISO 4624) |
Reaction to Fire
Bfl - s1 | (EN 13501-1) |
Chemical Resistance
Resistant to many chemicals. Contact Sika technical service for specific information.
Thermal Resistance
Exposure* | Dry heat |
Permanent | +50 °C |
Short-term max. 7 d | +80 °C |
Short-term moist/wet heat* up to +80 °C where exposure is only occasional (i.e. during steam cleaning etc.)
*No simultaneous chemical and mechanical exposure.
USGBC LEED Rating
Sikafloor®-305 W ESD conforms to the requirements of LEED EQ Credit 4.2: Low-Emitting Materials: Paints & Coatings. Reference Test Method 304: VOC Content < 100 g/l
Skid / Slip Resistance
R 11 | (DIN 51130) |
Electrostatic Behaviour
Resistance to ground1 | Rg < 109 Ω | (IEC 61340-4-1) |
Typical average resistance to ground2 | Rg < 105 - 106Ω | (DIN EN 1081) |
Body voltage generation2 | < 100 V | (IEC 61340-4-5) |
System Resistance (Person/Floor/Shoe)3 | < 35 M Ω | (IEC 61340-4-5) |
1 In accordance with IEC 61340-5-1 and ANSI/ESD S20.20.
2 Readings may vary, depending on ambient conditions (i.e. temperature, humidity) and measurement equipment.
3 Or < 109 Ω + body voltage generation of < 100 V, in case of readings > 35 M Ω.
Application
Ambient Air Temperature
+10 °C min. / +30 °C max.
Relative Air Humidity
During curing the humidity should not exceed 75 % max. Adequate fresh air ventilation or a dehumidifier must be provided to remove the excess moisture from the curing product.
Dew Point
Beware of condensation! The substrate and uncured floor must be at least 3 °C above dew point to reduce the risk of condensation or blooming on the floor finish.
Substrate Temperature
+10 °C min. / +30 °C max.
Substrate Moisture Content
<4 % pbw moisture content.
Test method: Sika Tramex Meter, CM-measurement or Oven-Dry-Method. No rising moisture according to ASTM (Polyethylene-sheet).
Waiting Time / Overcoating
Before applying Sikafloor®-327 on Sikafloor®-156/160/161 allow:
Substrate temperature | Minimum | Maximum |
+10°C | 24 hours | 4 days |
+20°C | 12 hours | 2 days |
+30°C | 8 hours | 1 days |
Before applying Sikafloor®-305 W ESD on Sikafloor®-327 allow:
Substrate temperature | Minimum | Maximum |
+10°C | 24 hours | 72 hours |
+20°C | 12 hours | 48 hours |
+30°C | 6 hours | 36 hours |
Before applying Sikafloor®-305 W ESD on Sikafloor®-305 W ESD allow:
Substrate temperature | Minimum | Maximum |
+10°C | 48 hours | 10 days |
+20°C | 24 hours | 8 days |
+30°C | 16 hours | 7 days |
Times are approximate and will be affected by changing ambient conditions particularly temperature and relative humidity.
Applied Product Ready for Use
Temperature | Foot traffic | Light traffic | Full cure |
+10°C | ~ 48 hours | ~ 5 days | ~ 10 days |
+20°C | ~ 24 hours | ~ 3 days | ~ 8 days |
+30°C | ~ 16 hours | ~ 2 days | ~ 7 days |
Note: Times are approximate and will be affected by changing ambient conditions
Consumption
Coating | Product | Consumption |
Primer | Sikafloor®-156/-160/-161 | 1-2 x ~ 0.3 - 0.5 kg/m² |
Levelling (if required) | Sikafloor®-156/-160/-161 levelling mortar | Refer to PDS of Sikafloor®-156/-160/-161 |
Base coat | Sikafloor®-327 | ~ 2.1 kg/m² (1.5 mm) |
Earthing connection | Sika® Earthing Kit | 1 earthing point per approx. 200 -300 m², min. 2 per room. |
Final conductive coating | Sikafloor®-305 W ESD | 1-2 x 0.18 – 0.2 kg/m²/layer |
These figures are theoretical and do not allow for any additional material due to surface porosity, surface profile, variations in level and wastage etc. When used in high wear conditions, e.g. castor chairs, a second layer with Sikafloor®-305 W ESD improves the mechanical properties of the floor covering. Lower consumption can cause roller marks, gloss differences and irregular surface structure, higher consumption result in water retention and can cause pigment floating as well as unsatisfactory conductivity.
CLEANING
Please refer to the Sikafloor® Cleaning Regime.