Parex® REVLANE+ SILOXANE IGNIFUGE TF

▪ ETA-04/0014 - PAREXTHERM EPS

▪ ETA-11/0110 - PAREXTHERM SW (Stone Wool)

• Thick, ready to use paste with acrylic and siloxane binders, minerals, pigments and additives.
• Water based.
• Specific additive: Biocide to protect the product from mildew and algae.

Shelf life 24 months from date of manufacture if stored in unopened original packing in dry, frost free conditions.

Dry frost free conditions

Density REVLANE+ IGNIFUGÉ TALOCHÉ FIN: 1.85 ± 0.10 g/cm³

• 24 hours under normal conditions.
• High humidity and low temperatures extend drying time.

COVERAGE

These values are provided as guidance only and may vary subject to substrate conditions, method of application and thickness applied.

• TALOCHE FIN: 10 to 12 m² per 25 kg container on a smooth flat surface.
• Spray applications will provide approx 20 % increased coverage.

EQUIPMENT REQUIRED

• Slow-speed electric mixer (< 300 rpm).
• Stainless steel smoothing or plastering trowel.
• Plastic float.
• Spray hopper or spray machine.
• Can be applied with an electric render machine after mixing.
• Clean equipment with water after use.

• The substrate must be flat, sound, clean and free from dirt and dust.
• The line and level of the substrate in new work must meet the requirements in BS 8000-3.
• The application of a layer of REVLANE REGULATEUR will generally be required first to prepare the surface, control suction and provide depth of colour in preparation for the top coat finish. Avoid application in direct sunlight in hot weather.

• Thoroughly mix the product in the container at slow speed until it is of an even consistency.
• In cold damp weather, 1 - 2 kg of PARITE+ ACCELERATEUR per 25 kg container may be added during mixing to accelerate drying. Refer to the corresponding data sheet.
• When mixing avoid creating air bubbles or foam.

• Apply the desired REVLANE TALOCHE finish in an even thickness, using a flexible stainless steel float. The thickness of the finish will be according to the size of grain. When floating the finish, if excess material splays over the top of the float, it is likely that too much material has been applied and thus needs to be removed until the material is the thickness of the grain size applied.
• Always maintain a wet edge and work to corners and joints.
• Finish off with a smooth plastic plastering float (a plastic float will roll the large aggregates more than a stainless steel trowel) in a regular motion or in the direction of the required dragged effect. Alternative effects can be created. Continuously dry clean the float during texturing. Use consistent pressure and motion to achieve the desired finish.
• For best colour consistency use the same batch numbers within a wall section.

Water soluble prior to drying.