Sikagard®-405 W
Sikagard®-405 W is a 1-part, water-based, modified acrylic resin coating. It contains an organic in-film preservative and provides a mid-sheen finish.
- Good resistance to repeated cleaning and disinfection regimes using mild detergents and cleaning solutions
- Tough
- High durability
- Good opacity (covering power)
- Good water vapour permeability
- Ultra-low VOC emissions
- Low odour
- Seamless
- Easy to clean
- Easy to apply
Usage
Sikagard®-405 W is used as a:- Top coat or standalone coating for walls and ceilings
- Concrete
- Bricks
- Gypsum and cement-based substrates
- Metal
- Timber
- Tiles
- Plastic
- The Product may only be used for interior applications.
- The Product may only be used by experienced professionals.
Advantages
- Good resistance to repeated cleaning and disinfection regimes using mild detergents and cleaning solutions
- Tough
- High durability
- Good opacity (covering power)
- Good water vapour permeability
- Ultra-low VOC emissions
- Low odour
- Seamless
- Easy to clean
- Easy to apply
Packaging
| One Part Container | 15 L (19.8 kg) drums |
Colour
Cured colour | White |
Product Details
ENVIRONMENTAL INFORMATION
Contributes towards satisfying Materials and Resources (MR) Credit: Building product disclosure and optimization — Environmental Product Declarations under LEED® v4
Contributes towards satisfying Materials and Resources (MR) Credit: Building Product Disclosure and Optimization — Material Ingredients under LEED® v4
Environmental Product Declaration (EPD) in accordance with EN 15804. EPD independently verified by Institut für Bauen und Umwelt e.V. (IBU)
APPROVALS / STANDARDS
Biological Resistance ISO 22196, SikaGard®-406W, IMSL, Report No. IMSL 2015/02/0
Crack-bridging test EN 1062-7, SikaGard®-403W, kiwa, Report No. P 10108-E
Fire testing ISO 476, SikaGard®-405W, Exova, Report No. 363979
Specular Gloss, Fineness of Grind, Wet Scrub Resistance and Contrast Ratio tests
Taint test EN 4120, SikaGard®-405W, Campden BRI, Report No. S/REP/138532/1
Triangle test EN 4120, SikaGard®-405 W, Campden BRI, Report No. S/REP/138532/1
Vapour permeability test EN 7783, SikaGard®-405W, 4ward, Certificate No. PO45008
Chemical Base
Water-based, acrylic copolymer dispersion
Shelf Life
12 months from date of production
Storage Conditions
The Product must be stored in original, unopened and undamaged sealed packaging in dry conditions at temperatures between +5 °C and +30 °C. Protect from direct sunlight and frost. Always refer to the packaging.
Density
1.31 kg/L | (EN ISO 2811-1) |
Solid content by mass
55 %
Solid content by volume
42 %
Tensile Strength
Unreinforced | 10 N/mm² |
Tensile adhesion strength
> 1.5 N/mm² (failure in concrete primed with Sika® Bonding Primer) | (EN 1542) |
Chemical Resistance
Good short-term resistance to mild acids, alkalis, cleaning agents and disinfectants. Please contact Sika Technical Services for specific information.
Disinfection with hydrogen peroxide vapour:
-
Resistant when using STERIS VHP technology.
-
Resistant to PEA vaporisation technology if a system structure with glass fibre reinforcement is used.
-
Resistant when using Oxypharm vaporiser type NOCOSPRAY under the following conditions:
| Disinfectant | Concentration | Setting at vaporiser | Contact time |
| NOCOLYSE Mint (6 %) | 1 ml/m3 | 20 m3 (1.5 min vaporisation) | 30 min |
| NOCOLYSE One Shot (12 %) | 3 ml/m3 (2 cycles) | 45 m3 (5 min vaporisation) | 30 min |
| NOCOLYSE Food (7.9 %) | 1 ml/m3 | 20 m3 (1.5 min vaporisation) | 30 min |
| NOCOLYSE Food (7.9 %) | 5 ml/m3 (2 cycles) | 75 m3 (5 min vaporisation) | 60 min |
Permeability to Water Vapour
51.5 g/m2 in 24 hours | (EN ISO 7783) |
Application
Layer Thickness
120 µm
Product Temperature
Maximum | +35 °C |
Minimum | +8 °C |
Ambient Air Temperature
Maximum | +35 °C |
Minimum | +8 °C |
Relative Air Humidity
Maximum | 80 % r.h. |
Dew Point
Beware of condensation. The substrate and uncured applied product must be at least +3 °C above dew point to reduce the risk of condensation on the surface of the applied product.
Substrate Temperature
Maximum | +35 °C |
Minimum | +8 °C |
Substrate Moisture Content
Visibly damp-free
Waiting Time / Overcoating
Before applying Sikagard®-405 W on Sikagard®-405 W, allow:
Temperature | Minimum | Maximum |
+10 °C | 4 hours | 7 days |
+20 °C | 2 hours | 7 days |
+30 °C | 1 hour | 7 days |
Before applying Sikagard®-405 W on Sikagard®-403 W, allow:
Temperature | Minimum | Maximum |
+10 °C | 4 hours | 7 days |
+20 °C | 1 hour | 7 days |
+30 °C | 1 hour | 7 days |
Note: Times are approximate and will be affected by changing ambient conditions, particularly temperature and relative humidity.
Applied Product Ready for Use
Temperature | Touch dry | Full cure |
+10 °C | 8 hours | 7 days |
+20 °C | 4 hours | 7 days |
+30 °C | 3 hours | 7 days |
Note: Times are approximate and will be affected by changing ambient conditions, particularly temperature and relative humidity.
Consumption
0.20 kg/m² per layer |
0.15 L/m² per layer |
Note: Consumption data is theoretical and does not allow for any additional material due to surface porosity, surface profile, variations in level, wastage or any other variations. Apply the Product to a test area to calculate the exact consumption for the specific substrate conditions and proposed application equipment.
MIXING
- IMPORTANT Avoid air entrapment. Use an electrical stirrer at low speed (300–400 rpm) to stir the Product until a uniform liquid has been achieved.
APPLICATION
WARNING
Hazardous respirable droplets may be formed when sprayed.
- Do not breathe spray or mist.
IMPORTANT
Reduced service life due to incorrect treatment of cracks
The incorrect assessment and treatment of cracks may lead to a reduced service life and reflective cracking.
- For static cracks, ensure the width is suitable for overcoating with Sikagard®-405 W.
- For dynamic cracks, ensure the movement is within the movement capacity of Sikagard®-405 W.
IMPORTANT
Risk of crazing due to excess moisture
Crazing may occur if coating undried surfaces.
- Ensure the entire surface is fully dry before proceeding.
- Allow new concrete substrates to cure or hydrate for a minimum of 10 days, and preferably 28 days.
IMPORTANT
Incompatibility with silicone sealants
Do not apply over silicone sealants.
IMPORTANT
Application on acoustic boards
Acoustic boards may lose some acoustic absorption after coating.
IMPORTANT
Do not thin or brush out like conventional paints
IMPORTANT
Gloss finish may vary
The gloss of the finish can vary with temperature, humidity and the absorbency of the substrate.
ROLLER APPLICATION
- IMPORTANT For aesthetic reasons, use the same roller type in the same areas. Apply the Product to the correct film thickness per layer with a short-pile roller.
AIRLESS SPRAY APPLICATION
This method leads to a smoother surface compared to roller application.
- IMPORTANT Use the same application type in the same areas. Apply the Product to the correct film thickness per layer with airless spraying application equipment, use tip sizes from 0.38–0.53 mm and a fan angle from 40° to 60°.
CLEANING OF TOOLS
Clean all tools and application equipment with water immediately after use. Hardened material can only be removed mechanically.