SikaCor® EG-1

• Approved according to German standard ‘TL/TP-KOR-Stahlbauten’, page 87.
• Suitability on galvanizing according German guideline 'AGK B1'.

3 years

In originally sealed containers in a cool and dry environment.

~1.6 kg/l

~60 % by volume

~77 % by weight

Weather, water, sewage, seawater, smoke, de-icing salts, acid and lye vapours, oils, grease and short term exposure to fuels and solvents.

Dry heat up to + 150 °C, short term up to + 180 °C Damp heat up to approx. + 50 °C In case of higher temperatures please consult Sika.

Sika® Thinner EG If necessary max. 5 % Sika® Thinner EG may be added to adapt the viscosity.

Min. + 5 °C

Max. 85 %, except the surface temperature is significantly higher than the dew point temperature, it shall be at least 3 K above dew point.

Min. + 5 °C

Min. until drying stage 6 is achieved

Max. 4 years

In case of longer waiting times please contact Sika.

Prior to further applications possible contamination must be removed.

Final drying time

Depending on film thickness and temperature full hardness is achieved after 1-2 weeks. Tests of the completed coating system should only be carried out after final curing.

Theoretical material-consumption/VOC without loss for medium dry film thickness:

With SikaCor® EG-1 up to 120 μm dry film thickness per operation can be achieved by spray.

Steel: Blast cleaning to Sa 2 ½ according to ISO 12944-4. Free from dirt, oil and grease. Hot dip galvanized steel, stainless steel and aluminium: Free from dirt, oil, grease and corrosion products.

In case of permanent immersion and condensation the surfaces must be slightly sweep blasted with a ferrite-free blasting abrasive.

Zinc spraying must be sealed and porefree. For contaminated surfaces e.g. galvanized or primed areas we recommend cleaning with SikaCor® Wash.

Stir component A very thoroughly using an electric mixer (start slowly, then increase up to approx. 300 rpm). Add component B carefully and mix both components very thoroughly (including sides and bottom of the container). Mix for at least 3 minutes until a homogeneous mixture is achieved. Fill mixed material into clean container and mix again shortly as described above. During mixing and handling of the materials always wear protective goggles, suitable gloves and other protective clothings.

The method of application has a major effect on achieving uniform thickness and appearance. Spray application will give the best results. The indicated dry film thickness is easily achieved by airless spray. Adding solvents reduces the sag resistance and the dry film thickness. In case of application by roller or brush, additional applications may become necessary to achieve the required coating thickness, depending on type of construction, site conditions, colour shade etc. Colour Stability: It is the natural tendency of epoxy products to discolorate (yellowing) whether used on internal or external areas. Therefore, any areas touched-up and repaired with the same colour at a later date may be obvious due to this colour change. Prior to major coating operations a test application on site may be useful to ensure the selected application method will provide the requested results.

By brush and roller Conventional high pressure spraying:

• Nozzle size 1.5 - 2.5 mm
• Pressure 3 - 5 bar
• Oil and water trap is compulsory

Airless-spraying:

• Pressure min. 180 bar
• Nozzle size 0.38 - 0.53 mm (0.015 - 0.021 inch)
• Spraying angle 40 °- 80 °

SikaCor® Cleaner